Home > Labs > Synthesis of Inverse Opals
Related labs: PMMA Synthesis, Diffraction, SEM
Printer Friendly

Synthesis of Inverse Opal Photonic Crystals

Procedure modified by George Lisensky, Jacob Horger and Jiaqi Luo, Beloit College, from the Inverse Opal Photonic Crystals Laboratory Guide by R. Schroden and N. Balakrishnan, University of Minnesota MRSEC, 2001.

A sol-gel synthesis using tetraethylorthosilicate and close-packed polymethylmethacrylate spheres as a template yields a dimensionally ordered porous silica solid.

Procedure

Wear eye protection

Chemical gloves
recommended

Fumehood recommended

Click image to play movie
Transfer a portion of your sample to two 1.7 mL microcentrifuge tubes. Always balance the centrifuge by pairing tubes such that opposing tubes have the same amount of solution. Spin your sample at 2000 rpm for 60 minutes or longer. (Spinning at 5000 rpm does not pack as well and spinning at 10,000 rpm will crush the product.)

Click image to play movie
Remove and discard the water above the polymerized polymethylmethacrylate spheres. Caution: Squeeze the dropper before immersing in the water, lower the dropper to just above the solid, and then release to remove the water. If you squeeze with the dropper in the water you will need to repeat the centrifuge step. Put the water in the organic waste.

Click image to play movie
Successful product will change colors with the angle of observation or lighting; the product should look irridescent.

Click image to play movie
Put the open centrifuge tube into a vacuum chamber for faster drying.

Click image to play movie
Dry the sample until it freely flows in the tube. This takes 1-2 hours at 15 torr.

Click image to play movie
Pour the solid into a combustion boat.

Click image to play movie
Prepare a well mixed solution of 1.0 mL 100% ethanol, 1.5 mL tetraethylorthosilicate, 1.0 mL 25% hydrochloric acid. (This mixture is enough for many samples but it must be freshly prepared.) Wet the spheres with the solution but once all the spheres are wet stop adding liquid or the product may be too dense.

Click image to play movie
Place the combustion boats into the quartz liner of a tube furnace (or a ventilated box furnace) in a hood.

Click image to play movie
Ramp the temperature at 2 degrees C/minute from room temperature to 300 degrees C to complete the silica formation. Hold at 300 degrees C for 2 hours. Ramp the temperature at 2 degrees C/minute to 550 degrees C to decompose the polymethylmethacrylate spheres. Hold at 550 degrees C overnight (ten hours). Cool the oven to room temperature.

Click image to play movie
Click image to play movie
High quality samples will be apparent by their opalescence.

SEM

Stick a portion of your sample to the carbon tape on the SEM holder and add your name to the sample map. Samples will then need to be sputtered since SiO2 is non-conducting. On our instrument (using 25kV with spotsize 27 and z 15mm) it should be possible to see holes at 3000x. Look carefully. Hole size is better measured using multiple holes in a line and then dividing by the number of holes measured. Be sure to include your analysis in your laboratory notebook.

Properties

Click image to play movie

Calculations and Conclusions

  1. Summarize the evidence that you made the desired product.
  2. Based on your SEM data, predict the absorption wavelength for air, ethanol, and toluene. How do you need to modify the equation for closed-packed spheres for the inverse material? How well do your predictions match the observed colors? Explain.

Materials

Click image to play movie


Developed in collaboration with the
University of Wisconsin Materials Research Science and Engineering Center